AISI 316L
Acciaio al Cr-Ni-Mo non temprabile a bassissimo Carbonio particolarmente adatto per costruzioni saldate, ottima resistenza alla corrosione intercristallina, impiegabile normalmente fino a 450°C.
CLASSIFICAZIONE:
| EN | ASTM | UNI | AFNOR | BSI | DIN | GOST | JIS | UNE |
| X2CrNiMo 17-12-2 | 316 L | X2CrNiMo 17-12 | Z 3 CND 17-11-02
Z 3 CND 17-12-02 |
316 S 11 | 1.4404 | 03 Ch17N 14 M2 | SUS 316 L | X2CrNiMo 17-12-03 |
| Euronorm | Nom. | AISI / ASTM / UNS |
| 1.4404 | X2CrNiMo17-12-2 | 316L |
MATERIE PRIME:
Possibilità di fornire formati standard o su specifica del cliente, per maggiori info clicca sul link
MATERIALI DI APPORTO:
| AISI 316L | ø DISP. 1.00/1.20/1.60/2.00/2.40/3.20/4.00 | CONF. KG 5,0 |
| AISI 316L | Ø DISP 0.80/1.00/1.20/1.60 BOB. KG. 15,0 | Ø DISP 2.00/2.40/3.20/4.00 BOB. KG. 25,0 |
-
NASTRI
PER QUOTAZIONE, DISPONIBILITA’ E TEMPI DI CONSEGNA
CONTATTACI SCRIVENDO A INFO@UNIVERSALD.IT O CHIAMA LO 02/95330307
COMPOSIZIONE CHIMICA:
| C | Si | Mn | Pmax | Smax | Cr | Ni | Mo | Ti | Cu | N(ppm) | N2 | Other | |
| <=0.030 | <=0.75 | <=2.00 | <=0.040 | <=0.030 | 16.00-18.00 | 10.00-12.00 | 2.00-2.50 | – | – | – | – | – | |
| <=0.030 | <=0.75 | <=2.00 | <=0.040 | <=0.030 | 16.50-18.00 | 10.00-11.00 | 2.00-2.50 | – | – | – | – | N(ppm) <1100 | |
| <=0.030 | <=0.75 | <=2.00 | <=0.040 | <=0.030 | 16.50-18.00 | 11.00-13.00 | 2.00-2.50 | – | – | – | – | N(ppm) <1100 | |
| <=0.030 | <=0.75 | <=2.00 | <=0.040 | 0.020-0.030 | 16.50-18.00 | 10.50-11.50 | 2.00-2.50 | – | – | – | – | N(ppm) <1100 | |
| <=0.030 | <=0.75 | <=2.00 | <=0.040 | <=0.030 | 16.50-18.00 | 11.00-13.00 | 2.00-2.50 | – | 0.5-1.0 | – | – | N(ppm) <1100 |
PER INFO SUL PRODOTTO E I SUOI UTILIZZI SCRIVI A: tecnico@universald.it
PER QUOTAZIONI E DISPONIBILITA’ DEI PRODOTTI
CONTATTACI ALLO 02/95330307 O SCRIVENDO A: info@universald.it
UNIVERSALD S.r.l.
Soluzioni per l’industria
20060 Bussero (MI) – Via P. Togliatti, 3 – Tel. 02/95330307-8 – Fax 02/95330309
E Mail info@universald.it – www.universald.i